Sabic醫(yī)療級(jí)塑料 PBT VALOX ? Resin HX312C
發(fā)布時(shí)間：2016-04-19 瀏覽次數(shù)：283 返回列表
|
|
|
Unreinforced PBT with release. For medical devices and pharmaceutical applications. Healthcare management of change, biocompatible (ISO 10993 or USP Class VI), food contact compliant. EtO and steam sterilizable.
|
|
|
|
TYPICAL PROPERTIES (1)
|
|
MECHANICAL
|
Value
|
Unit
|
Standard
|
|
Tensile Stress, yld, Type I, 50 mm/min
|
520
|
kgf/cm2
|
ASTM D 638
|
|
Tensile Stress, brk, Type I, 50 mm/min
|
300
|
kgf/cm2
|
ASTM D 638
|
|
Tensile Strain, yld, Type I, 50 mm/min
|
6
|
%
|
ASTM D 638
|
|
Tensile Strain, brk, Type I, 50 mm/min
|
25
|
%
|
ASTM D 638
|
|
Tensile Modulus, 50 mm/min
|
25400
|
kgf/cm2
|
ASTM D 638
|
|
Flexural Stress, yld, 1.3 mm/min, 50 mm span
|
830
|
kgf/cm2
|
ASTM D 790
|
|
Flexural Modulus, 1.3 mm/min, 50 mm span
|
23800
|
kgf/cm2
|
ASTM D 790
|
|
Tensile Stress, yield, 50 mm/min
|
58
|
MPa
|
ISO 527
|
|
Tensile Stress, break, 50 mm/min
|
30
|
MPa
|
ISO 527
|
|
Tensile Strain, yield, 50 mm/min
|
6
|
%
|
ISO 527
|
|
Tensile Strain, break, 50 mm/min
|
25
|
%
|
ISO 527
|
|
Tensile Modulus, 1 mm/min
|
2500
|
MPa
|
ISO 527
|
|
Flexural Stress, yield, 2 mm/min
|
85
|
MPa
|
ISO 178
|
|
Flexural Modulus, 2 mm/min
|
2400
|
MPa
|
ISO 178
|
|
IMPACT
|
Value
|
Unit
|
Standard
|
|
Izod Impact, notched, 23°C
|
5
|
cm-kgf/cm
|
ASTM D 256
|
|
Izod Impact, notched, -30°C
|
5
|
cm-kgf/cm
|
ASTM D 256
|
|
Instrumented Impact Total Energy, 23°C
|
407
|
cm-kgf
|
ASTM D 3763
|
|
Izod Impact, unnotched 80*10*4 +23°C
|
NB
|
kJ/m2
|
ISO 180/1U
|
|
Izod Impact, unnotched 80*10*4 -30°C
|
NB
|
kJ/m2
|
ISO 180/1U
|
|
Izod Impact, notched 80*10*4 +23°C
|
3
|
kJ/m2
|
ISO 180/1A
|
|
Izod Impact, notched 80*10*4 -30°C
|
3
|
kJ/m2
|
ISO 180/1A
|
|
Charpy 23°C, V-notch Edgew 80*10*4 sp=62mm
|
3
|
kJ/m2
|
ISO 179/1eA
|
|
Charpy -30°C, V-notch Edgew 80*10*4 sp=62mm
|
2
|
kJ/m2
|
ISO 179/1eA
|
|
Charpy 23°C, Unnotch Edgew 80*10*4 sp=62mm
|
NB
|
kJ/m2
|
ISO 179/1eU
|
|
Charpy -30°C, Unnotch Edgew 80*10*4 sp=62mm
|
NB
|
kJ/m2
|
ISO 179/1eU
|
|
THERMAL
|
Value
|
Unit
|
Standard
|
|
Vicat Softening Temp, Rate B/50
|
175
|
°C
|
ASTM D 1525
|
|
HDT, 1.82 MPa, 3.2mm, unannealed
|
54
|
°C
|
ASTM D 648
|
|
CTE, -40°C to 40°C, flow
|
1.E-04
|
1/°C
|
ASTM E 831
|
|
CTE, -40°C to 40°C, xflow
|
1.E-04
|
1/°C
|
ASTM E 831
|
|
CTE, 23°C to 80°C, flow
|
1.E-04
|
1/°C
|
ISO 11359-2
|
|
CTE, 23°C to 80°C, xflow
|
1.E-04
|
1/°C
|
ISO 11359-2
|
|
Vicat Softening Temp, Rate B/50
|
175
|
°C
|
ISO 306
|
|
Vicat Softening Temp, Rate B/120
|
165
|
°C
|
ISO 306
|
|
HDT/Ae, 1.8 MPa Edgew 120*10*4 sp=100mm
|
58
|
°C
|
ISO 75/Ae
|
|
PHYSICAL
|
Value
|
Unit
|
Standard
|
|
Specific Gravity
|
1.31
|
-
|
ASTM D 792
|
|
Mold Shrinkage, flow, 3.2 mm (5)
|
0.9 - 1.6
|
%
|
SABIC Method
|
|
Melt Flow Rate, 250°C/1.2 kgf
|
35
|
g/10 min
|
ASTM D 1238
|
|
Density
|
1.31
|
g/cm3
|
ISO 1183
|
|
Water Absorption, (23°C/sat)
|
0.35
|
%
|
ISO 62
|
|
Moisture Absorption (23°C / 50% RH)
|
0.08
|
%
|
ISO 62
|
|
Melt Volume Rate, MVR at 250°C/1.2 kg
|
31
|
cm3/10 min
|
ISO 1133
|
|
Source GMD, last updated:2011/03/14
|
|
Parameter
|
|
Injection Molding
|
Value
|
Unit
|
|
Drying Temperature
|
110 - 120
|
°C
|
|
Drying Time
|
2 - 4
|
hrs
|
|
Maximum Moisture Content
|
0.02
|
%
|
|
Melt Temperature
|
250 - 270
|
°C
|
|
Nozzle Temperature
|
240 - 260
|
°C
|
|
Front - Zone 3 Temperature
|
245 - 265
|
°C
|
|
Middle - Zone 2 Temperature
|
240 - 255
|
°C
|
|
Rear - Zone 1 Temperature
|
230 - 245
|
°C
|
|
Hopper Temperature
|
40 - 60
|
°C
|
|
Mold Temperature
|
40 - 100
|
°C
|
|
Source GMD, last updated:2011/03/14
|
轉(zhuǎn)載請(qǐng)注明：轉(zhuǎn)載自環(huán)球塑化資訊網(wǎng) http://pho2grapher.com/news/
本文鏈接：http://pho2grapher.com/b-shabo/news269597/
免責(zé)聲明：本文"Sabic醫(yī)療級(jí)塑料 PBT VALOX ? Resin HX312C"僅代表作者個(gè)人觀點(diǎn)，與環(huán)球塑化網(wǎng)無(wú)關(guān)。環(huán)球塑化網(wǎng)所轉(zhuǎn)載的內(nèi)容，其版權(quán)均由原作者和資料提供方所擁有！如因作品版權(quán)問(wèn)題需要處理，請(qǐng)與我們聯(lián)絡(luò)。電話：400-115-2868
|
簡(jiǎn)繁切換